Artículo de revista
Tratamiento de superficie de las restauraciones de porcelana feldespática y su implicancia en la propagación de las fallas estructurales propias del material
Surface treatment of feldespathic porcelain restoration and its implication in the spread of the material's structural failures
Barrionuevo, María Eugenia Alejandra
Universidad Nacional de Cuyo. Facultad de Odontología
- Enviar un email al autor
Colaboradores:
Ventrera, Verónica
Co-autor/a
Carrazco, María Elizabeth
Co-autor/a
Publicado en el 2014 en
Revista de la Facultad de Odontología,
Vol. 8, no. 2
Idioma:
Español
Resumen:
Español
Durante el proceso de elaboración de las porcelanas feldespáticas se producen en su interior micro rajaduras las cuales se propagan a través de la matriz vítrea aumentando la fragilidad del material cuando se lo expone a los esfuerzos mecánicos.
Las restauraciones rígidas de porcelanas feldespáticas son sometidas a distintos tratamientos en su superficie para aumentar la adhesión a las estructuras dentarias cuando son cementadas. Estos tratamientos son acondicionamiento con ácido fluorhídrico y microarenado.
Objetivos de este trabajo: 1. Evaluar la resistencia flexural de este material mediante ensayo mecánico en máquina Instron, previo tratamiento en su superficie
con ácido fluorhídrico y microarenado. 2. Observar al MEB las alteraciones de
superficie producidas por el microarenado y el ácido fluorhídrico. Los resultados
obtenidos demostraron que el tratamiento de microarenado produjo una reducción
de la resistencia flexural. El MEB confirmó la presencia de mayor cantidad
de microgrietas que podrían ser responsables de la disminución de la resistencia
flexural.
Inglés
In the preparation of feldspathic porcelains occur within microcracks,
which propagate through the glass matrix making them very fragile when
they are required mechanically.
The aim of this study was to evaluate the flexural strength of feldspathic
porcelain after being treated with sandblasting and hydrofluoric acid. The
samples were viewed with SEM to observe that these two treatments
altered form the porcelain surface.
Ceramic samples were prepared on which surface treatment is performed
with hydrofluoric acid and sandblasting. The samples thus prepared were
subjected to an Instron to determine the flexural strength.
The result was that the sandblasting treatment produced a highly significant
reduction in flexural strength.
SEM confirmed the presence of as many microgrietas responsible for the
decrease in flexural strength.
Disciplinas:
Palabras clave:
Descriptores:
Barrionuevo, María Eugenia Alejandra (2014) "Tratamiento de superficie de las restauraciones de porcelana feldespática y su implicancia en la propagación de las fallas estructurales propias del material: ". En: Revista de la Facultad de Odontología, Vol. 8, no. 2, p. 8-11.
Dirección URL del artículo: https://bdigital.uncu.edu.ar/7277.
Fecha de consulta del artículo: 19/04/24.
Este obra está bajo una Licencia Creative Commons Atribución-NoComercial-CompartirIgual 3.0 Unported.
Conozca más sobre esta licencia >